Resumen
OBJECTIVES: Bone replacement substitutes are almost unavoidable in augmentation procedures such as sinus grafting. The objective of the present study was to evaluate the osteoconductive capability of two different scaffold fillers in inducing newly formed bone in this procedure. MATERIAL AND METHODS: Sinus floor augmentation and implant placement were carried out bilaterally in 12 patients. Bovine bone mineral (BBM) was grafted on one side and beta-tricalcium phosphate (beta-TCP) on the contralateral side. Both were mixed (1:1 ratio) with autogenous cortical bone chips harvested from the mandible by a scraper. Hard tissue specimen cores were retrieved from the augmented sites (at the previous window area) at 12 months. Decalcified sections were stained with haematoxylin-eosin and the fraction area of new bone and filler particles was measured. In addition to the effect of the filler on new bone formation, the latter was tested to determine whether it correlated with the tissue depth and residual amount of the grafted material. RESULTS: Bone area fraction increased significantly from peripheral to deeper areas at both grafted sites in all cores: from 26.0 percent to 37.7 percent at the beta-TCP sites and from 33.5 percent to 53.7 percent at the BBM-grafted sites. At each depth the amount of new bone in BBM sites was significantly greater than that in TCP sites. However, the average area fraction of grafted material particles was similar in both fillers and all depth levels (beta-TCP=27.9-23.2 percent and BBM=29.2-22.6 percent, NS). A significant negative correlation was found between bone area fraction and particle area fraction at the middle (p=0.009) and deep (p=0.014) depths in the beta-TCP sites, but not at the BBM sites. CONCLUSION: At 12 months post-augmentation, the two examined bone fillers, beta-TCP and BBM, promoted new bone formation in sinus grafting but the amount of newly formed bone was significantly greater in BBM-grafted sites. However, both exhibited similar residual grafted material area fraction at this healing period. This could imply that BBM possesses better osteoconductive properties. (c) Blackwell Munksgaard, 2005. (AU)